A RESEARCH OF AIR PERMEABILITY OF POROUS SAMPLES WITH THE PURPOSE TO IDENTIFY OPTIMAL PARAMETERS

ДОСЛІДЖЕННЯ ПОВІТРОПРОНИКНОСТІ ПОРИСТИХ ЗРАЗКІВ З МЕТОЮ ВИЯВЛЕННЯ ОПТИМАЛЬНИХ ПАРАМЕТРІВ

V. Sychuk, O. Zabolotnyi
Lutsk National Technical University

Abstract

To reduce wear on the inner most responsible surface of a part (a nozzle of abrasive blasting machine) authors of the paper suggest to create an air layer on the mentioned above surface, this layer will act as a barrier between the abrasive and the working surface of the nozzle. As a consequence, part of the nozzle must be produced porous one. In this article we show the process of a research of the air permeability of porous powder samples with a porosity of 30%, 40%, 50% made of titanium powder PTH-1. Fractional composition of the powder of two types: -1mm...+0,63mm and -0,63mm...+0,4mm. There were researched properties and level of influence of fractional composition of powder and porosity of powder sample on pressure drop ΔP, which occurs when the flow of air pass through the porous element

Для зменшення зношування внутрішньої найбільш відповідальної поверхні деталі (сопла абразивоструменевої машини) авторами статті пропонується на вищезгаданій поверхні утворити повітряний прошарок, який буде виконувати роль бар’єру між абразивом і робочою поверхнею сопла. Як наслідок частину сопла необхідно виготовити пористою. В представленій статті показано процес дослідження повітропроникності пористих порошкових зразків з пористістю 30%, 40%, 50% виготовлених з титанового порошку марки ПТХ-1. Фракційний склад порошку: -1мм…+0,63мм і -0,63мм…+0,4мм. Досліджувався характер і ступінь впливу фракційного складу порошку і пористості порошкового зразка на перепад тиску ΔР, який виникає при проходженні потоку повітря через пористий зразок

Keywords

porosity, permeability, abrasive inkjet processing, wastage
пористість, повітропроникність, абразивоструменева обробка, зношування